Preparation of Ultra Fine Grain AA8006 Sheet by Accumulative Roll-Bonding
Original language description
Two pieces of the strip with dimensions of 250 mm x 50 mm x 2.5 mm were stacked to form a 5 mm thick specimen. Before stacking, the surfaces of the strips were degreased and wire-brushed to achieve good bonding. The pieces were joined together in the corners using Al wires and subsequently heated for 5 min to 200°C in an electrical furnace. After heating, the specimen was roll-bonded by rolling using a 50% reduction without lubricant. Five ARB cycles were successful. The initial material and the deformed microstructures were examined using electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM).
Czech name
Příprava plechu ze slitiny AA 8006 s ultrajemnými zrny metodou ARB
Czech description
Dva kousky plechu o rozměrech 250 mm x 50 mm x 2.5 mm byly odmaštěny, zdrsněny drátěným kartáčem a položeny na sebe. Po zahřátí po dobu 5 minut na teplotě 200°C v elektrické odporové peci byly obě části spojeny válcováním s redukcí 50% bez použití mazadla. Takto bylo úspěšně provedeno 5 cyklů. Výchozí i deformovaný materiál byly studovány pomocí difrakce zpětně odražených elektronů (EBSD) a transmisní elektronové mikroskopie (TEM).