EBSD Study of the Crack Propagation in the Fe3Al Based Intermetallic Alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F04%3A04105551" target="_blank" >RIV/68407700:21340/04:04105551 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
EBSD Study of the Crack Propagation in the Fe3Al Based Intermetallic Alloy
Original language description
The fracture properties of the hot rolled Fe-28at.%Al intermetallic alloy with the addition of chromium and cerium were studied using EBSD. Fractographic analysis carried out on fracture surfaces of ruptured specimens revealed several failure mechanismsof crack propagation. The main failure mechanism is transgranular cleavage.
Czech name
Studie šíření trhlin ve slitině na bázi Fe3Al pomocí EBSD
Czech description
Lomové chování intermetalické slitiny Fe-28at.%Al s příměsí chrómu a céru válcované za tepla bylo studováno pomocí EBSD. Lomové plochy porušených těles vykazují různou mikromorfologii lomu. Fraktografická analýza určila jako hlavní mikromechanismus lomutranskrystalické štěpení.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/GA106%2F02%2F0687" target="_blank" >GA106/02/0687: Improvement of properties of Fe3Al base intermetallics by thermal and mechanical treatment and by modified compositions</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2004
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)