Local Conditions at the Growing Fatigue Crack in CCT Specimens of Different Thicknesses

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F07%3A04135062" target="_blank" >RIV/68407700:21340/07:04135062 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Local Conditions at the Growing Fatigue Crack in CCT Specimens of Different Thicknesses

Original language description

An energetic approach based on local low-cycle fatigue conditions immediately at the crack front and on a critical value of plastic strain energy density is investigated using FEM simulation of the local loading conditions along the real fatigue crack front and experimental observation of growth of fatigue cracks in CCT specimens of 4 different thicknesses 5, 3, 1, and 0.5 mm

Czech name

Podmínky na čele rostoucí únavové trhliny v CCT tělesech různých tlouštěk

Czech description

V práci je zkoumáno energetické kritérium založené na představě lokální nízkocyklové únavy na čele trhliny a na kritické hodnotě hustoty plastické deformační energie. Lokální zatěžující podmínky na čele jsou zjištěny pomocí MKP, růst skutečné trhliny bylpozorován v CCT tělesech 4 různých tlouštěk 5, 3, 1, a 0,5 mm

Type

D - Article in proceedings

CEP classification

JL - Fatigue and fracture mechanics

OECD FORD branch

—

Project

—

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2007

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection

Proceedings of Workshop 2007

ISBN

978-80-01-03667-9

ISSN

—

e-ISSN

—

Number of pages

2

Pages from-to

358-359

Publisher name

ČVUT

Place of publication

Praha

Event location

Praha

Event date

Feb 19, 2007

Type of event by nationality

EUR - Evropská akce

UT code for WoS article

—