Degradation of Structure and Fatigue Properties of Structural CrMo Steels CSN 15313 and P91
Original language description
This paper summarizes the results of degradation study of two structural steels. Steels ČSN 15 313 a P91 were long-time annealed in laboratory with the aim to simulate the degradation of materials during operation service. Steel 15 313 was studied in following three states: the initial heat treatment, after annealing 650°C/500 h/air and after 650°C/1 000 h/air. Similarly, steel P91 was studied after the initial heat treatment, and after annealing 625°C/5 000 h/air. The results of structural and fatiguetests of these steels are included.
Czech name
Degradace strukturních a únavových vlastností konstrukčních CrMo ocelí ČSN 15313 a P91
Czech description
Článek shrnuje výsledky výzkumu degradace dvou konstrukčních ocelí. Oceli ČSN 15 313 a P91 byly podrobeny dlouhodobému laboratornímu žíhání, které simulovalo degradaci materiálu v provozních podmínkách. Ocel 15 313 tak byla studována ve třech stavech: výchozím a po žíhání 650°C/500 a 1000h/vzduch. Ocel P91 byla obdobně sledována ve stavu výchozím a po žíhání 625°C/5000h/vzduch. Tato práce zahrnuje tedy výsledky strukturní analýzy a únavových zkoušek.

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)