Fatigue and Fracture Toughness of Fe3Al Alloys with Additions of Zr and C
Original language description
Fracture behaviour of two intermetallic alloys based on Fe3Al with different Zr content was studied. On the alloy Fe-29.5Al-2.3Cr-0.63Zr-0.2C (at.%) (FA06Z), basic characterization of the microstructure by light and electron metallography was carried out. Tensile tests and fracture toughness tests were performed at 20, 200, 400, and 600°C. Previous fatigue experiments on the alloy Fe-31.5Al-3.5Cr-0.25Zr-0.2C (at.%) (FA02Z) were completed by fatigue tests at 150 and 600°C.
Czech name
Únava a lomová houževnatost slitin na bázi Fe3Al s přísadou Zr a C
Czech description
Byly studovány lomové vlastnosti dvou slitin na bázi Fe3Al s různým obsahem Zr. U slitiny Fe-29.5Al-2.3Cr-0.63Zr-0.2C (at.%) (FA06Z) byla provedena základní charakterizace mikrostruktury světelnou a elektronovou mikroskopií. Tahové zkoušky a zkoušky lomové houževnatosti byly provedeny při 20, 200, 400 a 600°C. Předcházející únavové experimenty na slitině Fe-31.5Al-3.5Cr-0.25Zr-0.2C (at.%) (FA02Z) byly doplněny

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)