Multi-Fractal Features of Fatigue Crack Surfaces in Relation to Crack Growth Rate

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F08%3A04150465" target="_blank" >RIV/68407700:21340/08:04150465 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Multi-Fractal Features of Fatigue Crack Surfaces in Relation to Crack Growth Rate
Original language description
Fatigue cracks in specimens from aluminium alloy were represented by SEM images and 3D reconstructions of fracture surface morphologies. A vector of fractal features characterized each image or 3D reconstruction of selected locations of fracture surfaces. Multilinear regression was used to express the relation between crack growt rate and feature vectors, with satisfactory results for both crack surface representations.
Czech name
Multifraktální příznaky únavových lomových ploch ve vztahu k rychlostí šíření trhliny
Czech description
Únavové lomy ve vzorcích z hliníkové slitiny byly representovány snímky z ŘEM a 3D rekonstrukcemi morfologie lomu. Obrazy resp. 3D rekonstrukce byly charakterizovány fraktálním příznakovým vektorem. Vazba mezi příznakovými vektory a rychlostí šíření trhliny byla vyjádřena multilineární regresí s uspokojivými výsledky v obou případech.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)