Stress Corrosion Cracking Testing in SCW - Results of SSRT Tests

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F11%3A00180255" target="_blank" >RIV/68407700:21340/11:00180255 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Stress Corrosion Cracking Testing in SCW - Results of SSRT Tests
Original language description
The presented paper summarizes the results of stress corrosion cracking (SCC) susceptibility tests in supercritical water (SCW) for austenitic alloys 316L, 316NG, 347HP and Alloy 690 with the aim to identify the maximum applicable SCW temperature and specific failure mechanisms prevailing during slow strain-rate tensile (SSRT) tests in ultra-pure demineralized SCW solution with controlled oxygen content. In addition to the strain rate, which was controlled by the crosshead speed, the oxygen content wasvaried in the series of tests in the case of austenitic stainless steel 316L. The fractography confirmed that failure was due to a combination of transgranular SCC and transgranular ductile fracture. Based on fractographic findings a phenomenological mapdescribing the SCC regime of SSRT test conditions was proposed for AISI 316L.
Czech name
—
Czech description
—

Project
—
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)<br>S - Specificky vyzkum na vysokych skolach

Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
The 5th International Symposium on Supercritical-Water-Cooled Reactors
ISBN
978-1-926773-02-5
ISSN
—
e-ISSN
—
Number of pages
16
Pages from-to
"P32"
Publisher name
Canadian Nuclear Society
Place of publication
Toronto
Event location
Vancouver
Event date
Mar 13, 2011
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—

Similar results(10)