Influence of Si and Fe on the distribution of intermetallic compounds in twin-roll cast Al-Mn-Zr alloys

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F12%3A00186894" target="_blank" >RIV/68407700:21340/12:00186894 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1016/j.jallcom.2011.11.101" target="_blank" >http://dx.doi.org/10.1016/j.jallcom.2011.11.101</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jallcom.2011.11.101" target="_blank" >10.1016/j.jallcom.2011.11.101</a>

Result language
angličtina
Original language name
Influence of Si and Fe on the distribution of intermetallic compounds in twin-roll cast Al-Mn-Zr alloys
Original language description
The aim of the experiments was to study the influence of Si and Fe on size and formation of secondary phases and recrystallization behaviour of Al-Mn-Zr alloys prepared by twin-roll casting (TRC) in the industrial conditions. A relatively high (0.5 wt.%)Si content and low (0.2 wt.%) Fe content in one of the alloys resulted in balancing of nucleation and dissolution rate for small particles. Hence a higher density of small particles was stable during the downstream processing, and this alloy showed improved recrystallization resistance.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)