Formation of Ni-Ti Intermetallics During Reactive Sintering at 500-650 °C

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F15%3A00239184" target="_blank" >RIV/68407700:21340/15:00239184 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1016/j.matchemphys.2015.02.007" target="_blank" >http://dx.doi.org/10.1016/j.matchemphys.2015.02.007</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matchemphys.2015.02.007" target="_blank" >10.1016/j.matchemphys.2015.02.007</a>

Result language
angličtina
Original language name
Formation of Ni-Ti Intermetallics During Reactive Sintering at 500-650 °C
Original language description
In this work, the formation of intermetallics in Ni-Ti system by reactive sintering at 500 and 650 degrees C was studied. Mechanism and kinetics of the reactions leading to Ni-Ti phases were determined by DTA and the application of an experimental modelconsisted of nickel-plated titanium. It was found that Ti2Ni phase forms already at 500 degrees C. At 650 degrees C this phase undergoes a reaction with nickel to NiTi and Ni3Ti. The reactions were determined to be diffusion-controlled. The formation ofNi3Ti contributes to the porosity evolution during reactive sintering production of NiTi alloy.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/GA14-03044S" target="_blank" >GA14-03044S: Preparation of NiTi shape memory alloys by reactive sintering</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)