Technological aspects of Fe-Al-Si intermetallic alloy preparation by mechanical alloying

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F19%3A00332962" target="_blank" >RIV/68407700:21340/19:00332962 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.4028/www.scientific.net/KEM.810.101" target="_blank" >https://doi.org/10.4028/www.scientific.net/KEM.810.101</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.810.101" target="_blank" >10.4028/www.scientific.net/KEM.810.101</a>

Result language
angličtina
Original language name
Technological aspects of Fe-Al-Si intermetallic alloy preparation by mechanical alloying
Original language description
In this paper, recently developed ternary FeAl20Si20 (wt.%) alloy with promising high-temperature oxidation and wear resistance was prepared by mechanical alloying in a high-energy ball mill. The possibility to speed-up the mechanical alloying process by replacing aluminium (and partly silicon) elemental powder by the pre-alloyed powder (AlSi30) with relatively fine dispersion of Si in the Al-Si eutectic was examined. The microstructure, phase composition and mechanical properties after various time of mechanical alloying were characterized. The effect of using the pre-alloyed powders on kinetics of mechanical alloying is compared with the results obtained on batches prepared from elemental powders.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2019
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)