Mid-infrared Diode Pumped Cr:ZnSe Laser Continuously Tunable from 2.1 μm up to 2.7 μm Operated at Room Temperature

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F22%3A00361640" target="_blank" >RIV/68407700:21340/22:00361640 - isvavai.cz</a>

  • Result on the web

    <a href="https://doi.org/10.1117/12.2659160" target="_blank" >https://doi.org/10.1117/12.2659160</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1117/12.2659160" target="_blank" >10.1117/12.2659160</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Mid-infrared Diode Pumped Cr:ZnSe Laser Continuously Tunable from 2.1 μm up to 2.7 μm Operated at Room Temperature

  • Original language description

    The spectroscopic and laser characteristics of optically polished Cr:ZnSe single crystals in four different lengths of 2, 3, 5, and 10 mm were investigated when pumping with a laser diode generating radiation at the wavelength of ~1.69 μm. The optimization from the point of laser efficiency was done in dependence on the crystal samples active length, effect of antireflection (AR) coatings, pumping pulse duration, and repetition rate. As a result, a 3 mm thick anti-reflection coated Cr:ZnSe crystal pumped by a laser diode with a pulse length of 20 ms and repetition rate of 10 Hz was chosen as the optimal. Using a 0.8 mm thick MgF2 birefringent filter the laser oscillations were continuously tunable from 2.1 μm up to 2.7 μm with the narrow spectral linewidth of ~5 nm and Gaussian beam profile. Maximum mean output power of ~0.35 W and maximum optical-to-optical slope efficiency of ~39% was obtained for 3 mm thick AR-coated sample which was ~28% and ~10% higher than that for uncoated sample of the same thickness, respectively. Continuously tunable laser oscillation wavelength was measured in the range of ~2.1-2.7 µm with the mean output power of P >= 150 mW within a ~5 nm linewidth. The absorption and fluorescence spectra as well as fluorescence lifetime were also measured. The Cr2+ fluorescence lifetime of ~7.2 µs measured for the 1 ns pulse excitation at room temperature (RT) was constant within the whole absorption band of 1.35–2.25 µm.

  • Czech name

  • Czech description

Classification

  • Type

    D - Article in proceedings

  • CEP classification

  • OECD FORD branch

    20201 - Electrical and electronic engineering

Result continuities

  • Project

    <a href="/en/project/EF16_019%2F0000778" target="_blank" >EF16_019/0000778: Center for advanced applied science</a><br>

  • Continuities

    P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Others

  • Publication year

    2022

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Article name in the collection

    Proc. SPIE 12502, 22nd Polish-Slovak-Czech Optical Conference on Wave and Quantum Aspects of Contemporary Optics

  • ISBN

    978-1-5106-6111-0

  • ISSN

    0277-786X

  • e-ISSN

    1996-756X

  • Number of pages

    12

  • Pages from-to

  • Publisher name

    SPIE

  • Place of publication

    Bellingham (stát Washington)

  • Event location

    Wojanów

  • Event date

    Sep 5, 2022

  • Type of event by nationality

    WRD - Celosvětová akce

  • UT code for WoS article

    000920988700001