Pressure-Dependent Viscosity of Powder Injection Moulding Compounds
Original language description
A single piston capillary rheometer was modified by addition of a second chamber with a restricting valve (developed at the Polymer Centre, Zlín, Czech Republic), which provides backpressure increasing the pressure in the melted material during the flowthrough the die. The Carreau-Yasuda model was employed to fit the measured viscosity data and determine the temperature and pressure coefficients for polyolefin based binder and its compounds with carbide powder. Both temperature and pressure sensitivitycoefficients are largely dependent on the structure of a polymer, which should be taken into account for binder-formation#s development. Increasing the loading level of the powder in the compound diminishes the pressure sensitivity of their flow properties.
Czech name
Tlakově závislá viskozita PIM materiálů
Czech description
V současnosti je výzkum Powder Injection Moulding (PIM) materiálů zaměřen především na podchycení kritických faktorů . Jedním z těchto klíčových aspektů je reologické chování PIM suspenzí. Viskozita těchto materiálů, závislá na rychlosti smykové deformace, teplotě a tlaku, je studována se specifickým zaměřením na kritické stupně plnění, kde je tokové chování navíc komplikováno tokovými nestabilitami.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
CD - Macromolecular chemistry
OECD FORD branch
—

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)