Kinetics of Dissolution of Na+[Carboxymethylcellulose] and Oxycellulose Mixture
Original language description
There was studied the kinetics of dissolution of solid films of NaCMC and OC prepared from their mixtures in water by fast plaster casting method on Petri dishes. The dependences of the kinetics parameters of the process (tQ, uOC, deltaHnerovná se i,j, RAdelta,i) on the given polymer compositions were determined. It has been found, that internal pressure in the solid swollen layer decreased with increasing content of OC in the mixture as well as the activation enthalpy of diffusion connected with swelling deltaH does not equal D,s.
Czech name
Kinetika rozpouštění směsi sodné soli karboxymethylcelulózy a oxycelulózy
Czech description
Byly proměřeny kinetické křivky rozpouštění tuhých filmů sodné soli karboxymethylcellulózy a oxycelulózy připravených jejích směšování ve formě gelů. byly stanoveny parametry procesu rozpouštění (tQ, uOC, deltaH nerovná se i,j, RAdelta,i) pro přesně definované kompozice složení směsi. Bylo zjištěno, že vnitřní tlak tuhé naboptnalé vrstvičky klesá s narůstajícím obsahem oxycelulózy ve směsi a současně narůstá aktivační entalpie difuze spojené s botnáním deltaH nerovná se D,s.