Fatigue Life of Thermoset Composite Materials

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F19%3A63523328" target="_blank" >RIV/70883521:28110/19:63523328 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Fatigue Life of Thermoset Composite Materials

Original language description

This article deals with the lifetime of laminated materials produced by different production technologies (hand lamination technology, vacuum bagging technology and prepreg technology with curing in the oven) during cyclic repeated bending stress. Like tested materials composite systems were chosen with epoxy matrix and carbon reinforcement (Kordcarbon CC200T, epoxy resin with trade name L285) and second composite epoxy system with glass reinforcement (Quadra-axial glass fabric, named Saertex Q-E-820, epoxy resin Biresin CR 82 and third prepreg systems (unidirectional prepreg, trade name Deltapreg VV430U-DT860W-39% and prepreg system with glass fabric VV320P_DT806R-37%). Fatigue tests were performed by cyclic bending loads during a three-point arrangement on a universal servo-hydraulic testing machine INSTRON 8871. Experimentally the number of cycles fracture of the material was determined at 90 % and 80 % of the maximum breaking load.

Czech name

—

Czech description

—

Type

O - Miscellaneous

CEP classification

—

OECD FORD branch

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Project

—

Continuities

S - Specificky vyzkum na vysokych skolach

Publication year

2019

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů