Microstructural Investigation and Mechanical Testing of an Ultrafine-grained Austenitic Stainless Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00398461" target="_blank" >RIV/68081723:_____/13:00398461 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructural Investigation and Mechanical Testing of an Ultrafine-grained Austenitic Stainless Steel

Popis výsledku v původním jazyce

Special thermomechanical treatment based on high degree deformation followed by reversion annealing was applied to 301LN austenitic stainless steel to achieve ultrafine-grained (UFG) structure with considerably enhanced mechanical properties. Two different conditions of the thermomechanical treatment were adopted and resulting microstructures with different grain sizes were characterised by optical and high resolution scanning electron microscopy (SEM-FEG). Hardness measurements and tensile tests were performed to characterize mechanical properties. To reveal structural changes induced during thermomechanical treatment and during tensile tests a magnetic induction method was additionally applied. Experimental study validated the ability of the above special treatment to produce austenitic stainless steel with grain size about 1.4 m which exhibits tensile strength about 1000MPa while ductility remains on level about 60 %. The results obtained for both thermomechanical conditions are com

Název v anglickém jazyce

Microstructural Investigation and Mechanical Testing of an Ultrafine-grained Austenitic Stainless Steel

Popis výsledku anglicky

Special thermomechanical treatment based on high degree deformation followed by reversion annealing was applied to 301LN austenitic stainless steel to achieve ultrafine-grained (UFG) structure with considerably enhanced mechanical properties. Two different conditions of the thermomechanical treatment were adopted and resulting microstructures with different grain sizes were characterised by optical and high resolution scanning electron microscopy (SEM-FEG). Hardness measurements and tensile tests were performed to characterize mechanical properties. To reveal structural changes induced during thermomechanical treatment and during tensile tests a magnetic induction method was additionally applied. Experimental study validated the ability of the above special treatment to produce austenitic stainless steel with grain size about 1.4 m which exhibits tensile strength about 1000MPa while ductility remains on level about 60 %. The results obtained for both thermomechanical conditions are com

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA13-32665S" target="_blank" >GA13-32665S: Mechanismy únavového poškozování u ultrajemnozrnných nerezavějících ocelí</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANOCON 2013 Conference Proceedings

ISBN

978-80-87294-44-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Tanger

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

16. 10. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—