Fabrication of Al-Mg solid solution by friction stir selective alloying

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216224%3A14310%2F22%3A00125096" target="_blank" >RIV/00216224:14310/22:00125096 - isvavai.cz</a>
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S0167577X21017717?dgcid=rss_sd_all#" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0167577X21017717?dgcid=rss_sd_all#</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matlet.2021.131073" target="_blank" >10.1016/j.matlet.2021.131073</a>

Result language
angličtina
Original language name
Fabrication of Al-Mg solid solution by friction stir selective alloying
Original language description
This study reports the fabrication of an Al-Mg solid solution layer containing ∼2 at.% Mg on pure Al substrate by a solid-state processing technique called friction stir selective alloying. Accordingly, a machined groove on the surface of Al substrate was filled by a bulk Mg block and friction stir processing was applied to form Al-Mg solid solution. The XRD/EDS results revealed formation of solid solution structure in the stirred zone of the alloyed sample. Furthermore, the hardness of the prepared Al-Mg solid solution (∼55.8 HV) was more than twice greater than the hardness of the FSPed neat sample (∼25.0 HV).
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
10305 - Fluids and plasma physics (including surface physics)

Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2022
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)