On crack path in fibres-reinforced ceramic composites

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU47398" target="_blank" >RIV/00216305:26210/05:PU47398 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
On crack path in fibres-reinforced ceramic composites
Original language description
Stability and/or instability of the straight micro-crack paths is investigated for a periodic array of originally collinear, slowly growing microcracks with fibres located in between the neighbouring micro-cracks tips. The relevant application e.g. refers to matrix cracking in 90"a plies of cross-ply ceramic composites.
Czech name
O směrové stabilitě trhlin v kompozitech zpevněných vlákny
Czech description
Stability and/or instability of the straight micro-crack paths is investigated for a periodic array of originally collinear, slowly growing microcracks with fibres located in between the neighbouring micro-cracks tips. The relevant application e.g. refers to matrix cracking in 90"a plies of cross-ply ceramic composites.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—

Project
<a href="/en/project/GA101%2F02%2F0683" target="_blank" >GA101/02/0683: Crack/microcrack behaviour in selected brittle matrix composites</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)