Influence of Plasma-Nitriding Surface Layer on Fatigue Life of Steel Specimens under Biaxial Loading

Result code in IS VaVaI

RIV/00216305:26210/05:PU54132 - isvavai.cz

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Influence of Plasma-Nitriding Surface Layer on Fatigue Life of Steel Specimens under Biaxial Loading

Original language description

The paper presents results of experimental investigation of fatigue resistance of virgin and plasma-nitridized specimens made of the low-alloy high-strength steel. The specimens were subjected to in-phase combined bending-torsion loading. The presence ofsurface layers has significantly improved the fatigue life in the high-cycle region. The prediction of biaxial fatigue life on the basis of uniaxial data was more successful when using the Papadopoulos criterion than the Gough-Pollard criterion.

Czech name

Vliv plazmové nitridace ocelových vzorků na únavovou životnost při biaxiálním zatěžování

Czech description

Vliv plazmové nitridace ocelových vzorků na únavovou životnost při biaxiálním zatěžování

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JL - Fatigue and fracture mechanics

OECD FORD branch

—

Project

GA106/05/0550: Application of Quantitative Fractography and Stereology to Crack Path Analysis in Biaxial Fatigue

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year

2005

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Materiálové inžinierstvo

ISSN

1335-0803

e-ISSN

—

Volume of the periodical

12

Issue of the periodical within the volume

3

Country of publishing house

SK - SLOVAKIA

Number of pages

3

Pages from-to

123-125

UT code for WoS article

—

EID of the result in the Scopus database

—