INFLUENCE OF HEAT TREATMENT ON THE MICROSTRUCTURE OF AZ 91 HP ALLOY

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU62289" target="_blank" >RIV/00216305:26210/05:PU62289 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
INFLUENCE OF HEAT TREATMENT ON THE MICROSTRUCTURE OF AZ 91 HP ALLOY
Original language description
This contribution deals with the evolution of microstructure of the magnesium alloy AZ 91 HP due to different heat treatment done in the foundry at the producer's site. There were two variants of the heat treatment (annealing) intended to dissolve the massive Mg17Al12 precipitates and to avoid their repetitive formation. The dissolution of the Mg17Al12 precipitates was observed in both cases and the resultant microstructures were similar.
Czech name
Vliv tepelného zpracování na mikrostrukturu slitiny AZ 91 HP
Czech description
Příspěvek se zabývá vlivem dvou variant tepelného zpracování na mikrostrukturu slitiny AZ 91 HP, provedené jejím výrobcem. Cílem obou variant tepelného zpracování (žíhání) bylo rozpustit precipitáty fáze Mg17Al12 a zabránit její opětné precipitaci. Tohoto cíle bylo dosaženo v obou případech, přičemž výsledné mikrostruktury jsou téměř srovnatelné.

Project
<a href="/en/project/1M0556" target="_blank" >1M0556: Eco-Centre for Applied Research of Non-Ferrous Metals</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)