Cyclic stress-strain response and changes of microstructure of UFG copper

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU65353" target="_blank" >RIV/00216305:26210/05:PU65353 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Cyclic stress-strain response and changes of microstructure of UFG copper
Original language description
Cyclic stress-strain response of UFG Cu under stress controlled loading changes qualitatively with the stress amplitude. For low stress amplitudes continuous cyclic hardening during the whole fatigue life can be seen. Nearly stable cyclic behaviour can be found for intermediate stress amplitudes and for high stress amplitudes pronounced cyclic softening is a characteristic feature. No detectable changes of microstructure were revealed by EBSD.
Czech name
Cyklická napěťově deformační odezva a mikrostrukturní změny v ultrajemnozrnné mědi
Czech description
Cyklická napěťově deformační odezva ultrajemnozrnné mědi při řízeném zatěžování se kvalitativně mění s amplitudou napětí. Pro nízké amplitudy napětí je vidět cyklické zpevnění během celého únavového zatěžování. Téměř stabilní cyklické chování bylo pozorováno v oblastech středních hodnot amplitudy napětí a pro vysoké amplitudy napětí je charakteristické cyklické změkčení. Pomocí EBSD techniky nebyly zjištěny žádné mikrostrukturní změny během cyklického zatěžování.

Project
<a href="/en/project/GD106%2F05%2FH008" target="_blank" >GD106/05/H008: Multiscale design of advanced materials</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)