Fatigue Lifetime of ADI from Ultimate Tensile Strength to Permanent Fatigue Limit

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F07%3APU73322" target="_blank" >RIV/00216305:26210/07:PU73322 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Fatigue Lifetime of ADI from Ultimate Tensile Strength to Permanent Fatigue Limit
Original language description
Isothermally treated ADI (austempered ductile iron) is preferably used for dynamically loaded components (e.g. gear and traversing wheels, crankshafts, swivel pins, rail brakes etc.) in very large lifetime range, therefore its fatigue properties are studied in very wide region of cycles to fracture. The aim of the paper consists in determination of S-N curve for the whole range of ADI lifetime from 0.5 to 100 millions cycles to fracture at symmetric push-pull loading at room temperature.
Czech name
Únavová životnost ADI pro celou oblast životnosti.
Czech description
Perspektivní materiál využitelný v mnoha odvětvích strojírenství, stavebnictví a dopravy je litina s kuličkovým grafitem (LKG) a její izotermicky zušlechtěná varianta (ADI). Její velkou předností oproti jiným druhům litin je příznivý tvar grafitu, kterýumožňuje plně využít mechanických vlastností kovové matrice. Cílem této práce je stanovení Wöhlerovy křivky pro celou oblast životnosti ADI při symetrickém namáhání tah-tlak za normální teploty. Dále pak proložení experimentálně zjištěnými body vhodnou regresní funkci a zjištění jejich parametrů.

Project
<a href="/en/project/GA106%2F03%2F1265" target="_blank" >GA106/03/1265: Influence of selected factors on fatigue properties of ADI</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)