Diffusion in Al-Ni and Al-NiCr Interfaces at Moderated Temperatures
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU83552" target="_blank" >RIV/00216305:26210/09:PU83552 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Diffusion in Al-Ni and Al-NiCr Interfaces at Moderated Temperatures
Original language description
The diffusion couples for experimental study were prepared by HVOF spraying of nickel and nickel with 20wt.% of chromium powders onto the aluminium steet s surface. The interfaces with sharp gradient of chemical concentration of these elements were prepared. Annealing at the temperatures 600oC and 630oC, close to the Al+Al3Ni eutectic melting point (639,9oC), with different dwell times were realized. The reactants during the annealing diffuse and create layers of Al3Ni2 and Al3Ni intermediate phase compositions. Moreover, nickel without assistance of chromium diffuses preferably by using grain boundaries into aluminium substrate and produces the strengthening of the substrate by stable Al3Ni and metastable Al9Ni2 particles. The microstructures were obtained by scanning electron microscope. Layer theckness measurements were realized by means of image analyses. Chemical composition was estimated by energy dispersive microanalysis measurements. According to the results of these analyses p
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JI - Composite materials
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů