MULTICOMPONENT ALLOY POWDERS PREPARATION BY MECHANICAL ALLOYING

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F15%3APU114886" target="_blank" >RIV/00216305:26210/15:PU114886 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
MULTICOMPONENT ALLOY POWDERS PREPARATION BY MECHANICAL ALLOYING
Original language description
In the last decade, multicomponent alloys arisen as new promising family of materials. The effect of milling parameters, namely milling balls size, milling speed and time on synthesis of inequiatomic AlCoCrFeNiTi0,5 mechanically alloyed (MA) powders in planetary ball mill were studied. Alloying behaviour, morphology, size and homogeneity of powders were observed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). During MA, a supersaturated Cr based solid solution with BCC structure was formed after 24 hours of milling, with significantly reduced grain size. It was revealed, that selection of milling conditions have a great influence on milled powders properties. In general softer milling condition result in decreased particle size and homogeneity
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)