Characterization of Electroless Ni–P Coating Prepared on a Wrought ZE10 Magnesium Alloy
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F18%3APU127487" target="_blank" >RIV/00216305:26310/18:PU127487 - isvavai.cz</a>
Result on the web
<a href="http://www.mdpi.com/2079-6412/8/3/96" target="_blank" >http://www.mdpi.com/2079-6412/8/3/96</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/coatings8030096" target="_blank" >10.3390/coatings8030096</a>
Alternative languages
Result language
angličtina
Original language name
Characterization of Electroless Ni–P Coating Prepared on a Wrought ZE10 Magnesium Alloy
Original language description
Electroless low-phosphorus Ni–P coating was deposited on a wrought ZE10 magnesium alloy including an advanced pre-treatment of the material surface before deposition. Uniform Ni–P coating with an average thickness of 10 µm was formed by 95.6 wt % Ni and 4.4 wt % P. The content of Ni and P was homogeneous in the entire cross-section of the coating. Applying the Ni–P coating to the magnesium substrate, the surface microhardness increased from 60 ± 4 HV 0.025 to 690 ± 30 HV 0.025. Using the scratch test, it was determined that deposited Ni–P coating exhibits a high degree of adhesion to the magnesium substrate. Electrochemical corrosion properties of Ni–P coating were analyzed using the polarization tests in 0.1 M NaCl, while the deposited Ni–P coating showed an improvement of the corrosion resistance when compared to the ZE10 magnesium alloy. Using the scanning electron microscopy analysis, it was determined that the fine morphology of the deposited Ni–P coating did not contain visible microcavities. The absence of macrodefects due to the adequate pre-treatment before coating was reflected on the mechanism of the coated ZE10 degradation in a 0.1 M NaCl solution.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20506 - Coating and films
Result continuities
Project
<a href="/en/project/LO1211" target="_blank" >LO1211: Materials Research Centre at FCH BUT- Sustainability and Development</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Others
Publication year
2018
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Coatings, MDPI
ISSN
2079-6412
e-ISSN
—
Volume of the periodical
3
Issue of the periodical within the volume
8
Country of publishing house
CH - SWITZERLAND
Number of pages
14
Pages from-to
1-14
UT code for WoS article
000428506500012
EID of the result in the Scopus database
2-s2.0-85051542113