Morphogenesis and viscoelastic properties of dental dimethacrylate networks

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU110920" target="_blank" >RIV/00216305:26620/14:PU110920 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Morphogenesis and viscoelastic properties of dental dimethacrylate networks
Original language description
This contribution aims with investigation of the (co)polymerization kinetics of the dimethacrylate monomers, used, inter alia, in the field of restorative dentistry. The kinetics and mechanisms of tetrafunctional networks morphogenesis were studied regarding the structural differences and the molar ratio of the comonomers used. Then, time and temperature dependences of the viscoelastic moduli of these systems were determined in order to quantify the relationship between the supramolecular structure andstorage and loss moduli. In order to clarify the characteristics mentioned above, various methods of structural and thermomechanical analysis were employed. (Co)Polymerization kinetics was studied by differential photocalorimetry (DPC). Double bond conversion was determined by both the kinetic measurements and by the infrared spectroscopy (FTIR). Viscoelastic parameters were measured by the methods of dynamic-mechanical analysis (DMA). The kinetics of the decomposition process was invest
Czech name
—
Czech description
—

Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)