Crack closure phenomenon in a carbon cast steel with practical engineering impacts
Original language description
Fatigue crack growth in Paris stable and near-threshold regions in a carbon cast steel were evaluated considering crack closure effects due to fretting oxidation. A specific case of gradual reduction of crack closure effect during leaking of oil to the fatigue crack tip is described and discussed.
Czech name
Jev uzavírání trhlin v uhlíkové lité oceli s praktickými inženýrskými dopady
Czech description
Byla hodnocena rychlost růstu únavových trhlin ve stabilní parisově oblasti a v prahové oblasti v uhlíkové lité oceli s uvážením efektu uzavírání trhlin v důsledku třecí oxidace. Je popsán a diskutován specifický případ postupného snižování efektu uzavírání trhliny v důsledku průniku oleje k čelu únavové trhliny.

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
Proceedings of the 17th European Conference on Fracture
ISBN
978-80-214-3692-3
ISSN
—
e-ISSN
—
Number of pages
7
Pages from-to
—
Publisher name
VUTIUM Brno
Place of publication
Brno
Event location
Brno
Event date
Jan 1, 2008
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—

Similar results(10)