Evaluation of Hydrogen Induced Cracks in Gas Pipeline Steels and Influence of Microstructure

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F09%3A%230000135" target="_blank" >RIV/25797000:_____/09:#0000135 - isvavai.cz</a>
Alternative codes found
RIV/25797000:_____/09:#0000178
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Evaluation of Hydrogen Induced Cracks in Gas Pipeline Steels and Influence of Microstructure
Original language description
This article deals with evaluation and measurement of hydrogen induced cracks in steel strips for gas pipelines. Strips were made from steels L360MB, L450MB, L485MB. Quantitative values of hydrogen induced cracking are given into correlation with microstructure. Main reason for susceptibility of these steels to hydrogen induced cracking was found in pearlitic banding.
Czech name
Hodnocení vodíkem indukovaných trhlin v ocelích pro plynovody a vliv mikrostruktury
Czech description
Článek se zabývá hodnocením a měřením vodíkem indukovaných trhlin v ocelových pásech ze kterých se vyrábí plynovodní potrubí. Pásy byly vyrobeny z ocelí L360MB, L450MB a L485MB. Kvantitativní hodnoty vodíkem indukovaného praskání jsou dávány do korelaces mikrostrukturou. Hlavní důvod pro náchylnost těchto ocelí k vodíkem indukovanému praskání byl shledán v perlitickém pásování.