Numerical Simulations of Effects of Furnace Lining Radiation on 34CrNiMo6 Ingots
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F11%3A%230000270" target="_blank" >RIV/26316919:_____/11:#0000270 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Numerical Simulations of Effects of Furnace Lining Radiation on 34CrNiMo6 Ingots
Original language description
The purpose of this study was to identify possible causes of formation of longitudinal surface cracks occurring during early stages of ingot forging. However, these cracks need not necessarily occur during forging or as a result of poor quality of the surface in metallurgical terms. Under certain conditions, they may form even as the the ingot is being heated in the furnace to the forging temperature. The cracks probably form within a few minutes of placement of the ingot in the furnace due to the temperature gradient which is most severe on the ingot surface. The numerical model was created to represent the case of placing two ingots in a furnace. Ingots cast from 34CrNiMo6 steel were used for simulation of a process where the ingot is cooled upon casting to no more than 600°C and then placed in a furnace at 1,100 - 1,200°C. Reference points were selected on the ingots either on or just below their surface. Numerical simulations in DEFORM and MSC.Marc/Mentat programs were used to anal
Czech name
—
Czech description
—
Classification
Type
D - Article in proceedings
CEP classification
JP - Industrial processes and processing
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/FR-TI1%2F490" target="_blank" >FR-TI1/490: *Increase of competitice adventage of steel rolls</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Article name in the collection
METAL 2011
ISBN
978-80-87294-24-6
ISSN
—
e-ISSN
—
Number of pages
6
Pages from-to
266-271
Publisher name
TANGER spol. s r.o.
Place of publication
Ostrava
Event location
Brno, Česká republika
Event date
May 18, 2011
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—