Fatigue performance of blade steel T552 in a corrosive environment

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F16%3AN0000097" target="_blank" >RIV/26722445:_____/16:N0000097 - isvavai.cz</a>
Alternative codes found
RIV/26722445:_____/16:N0000038
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Fatigue performance of blade steel T552 in a corrosive environment
Original language description
This contribution is based on an experimental programme which deals with the issue of blade steel T552 corrosion fatigue damage. The specimens were taken from a reference material delivered for blade production and tested in a corrosion cell under pre-stress of 300 MPa. A chloride solution of 35 ppm was chosen as the environment at a temperature of 80°C. Such an environment can be considered as the limit state that should not occur during the operating regime. The results are summarized and compared with experiments conducted at another workplace.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
4th International Conference Recent Trends in Structural Materials
ISBN
978-80-87294-69-7
ISSN
—
e-ISSN
—
Number of pages
6
Pages from-to
1-6
Publisher name
Tanger Ltd
Place of publication
Ostrava
Event location
Plzeň
Event date
Nov 9, 2016
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—

Similar results(10)