Fatigue performance of blade steel T552 in a corrosive environment

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F17%3AN0000032" target="_blank" >RIV/47718684:_____/17:N0000032 - isvavai.cz</a>
Result on the web
<a href="http://iopscience.iop.org/article/10.1088/1757-899X/179/1/012034" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/179/1/012034</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1757-899X/179/1/012034" target="_blank" >10.1088/1757-899X/179/1/012034</a>

Result language
angličtina
Original language name
Fatigue performance of blade steel T552 in a corrosive environment
Original language description
This contribution is based on an experimental programme which deals with the issue of blade steel T552 corrosion fatigue damage. The specimens were taken from a reference material delivered for blade production and tested in a corrosion cell under pre-stress of 300 MPa. A chloride solution of 35 ppm was chosen as the environment at a temperature of 80 °C. Such an environment can be considered as the limit state that should not occur during the operating regime. The results are summarized and compared with experiments conducted at another workplace.
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20501 - Materials engineering

Project
<a href="/en/project/TA04020685" target="_blank" >TA04020685: Research and development of a corrosion resistant low pressure steam turbine blade</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)