Initiation of LME crack in ferritic martensitic steel in liquid lead-bismuth
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F18%3AN0000028" target="_blank" >RIV/26722445:_____/18:N0000028 - isvavai.cz</a>
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S002231151830895X" target="_blank" >https://www.sciencedirect.com/science/article/pii/S002231151830895X</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jnucmat.2018.09.033" target="_blank" >10.1016/j.jnucmat.2018.09.033</a>
Alternative languages
Result language
angličtina
Original language name
Initiation of LME crack in ferritic martensitic steel in liquid lead-bismuth
Original language description
This work is aimed at fundamental understanding of the T91 steel cracking mechanisms in liquid PbBi eutectic. In particular, the crack initiation was studied by means of Constant Extension Rate Tensile (CERT) tests with flat tapered specimens in PbBi at 300 degrees C with oxygen content 3 x 10(-7) - 6 x 10(-6) wt. % and in air, up to rupture and maximum load. The tapered specimens were meant to create a uniform variation of stress along the gauge length and the threshold stress of the crack initiation was determined. The performance of the steel was affected by the environment. The threshold stress decreased and cracking character changed in PbBi when compared to the testing in air. Post-test examinations carrying out with SEM equipped with FIB found shallow cracks from broken oxide having ductile propagation and a grain-size-deep crack of inter-lath martensite path in the plastic strain region. The cracking stress-strain conditions and the role of oxide rupture causing wetting, as the cracking precursors, are discussed.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20501 - Materials engineering
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2018
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Journal of Nuclear Materials
ISSN
0022-3115
e-ISSN
1873-4820
Volume of the periodical
511
Issue of the periodical within the volume
December
Country of publishing house
NL - THE KINGDOM OF THE NETHERLANDS
Number of pages
14
Pages from-to
549-472
UT code for WoS article
000447796300046
EID of the result in the Scopus database
2-s2.0-85054293378