Tensile behavior of natural fabric reinforced composite

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F16%3A00000368" target="_blank" >RIV/46747885:24210/16:00000368 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Tensile behavior of natural fabric reinforced composite

Original language description

Tensile behavior of natural fabric reinforced composite were investigated in this work. Natural fabric such as flax and jute were considered in bi-axial plain reinforcement in matrix of acrylic resin. The composite are prepared in hand layup techniques. Fabric weight fraction of 7 % was used in the matrix of composite. The samples were treated at RT and 60°C for the final fabrication. Tensile test were carried out on the samples with dimension 200x30x5.5 mm/min. The result of flax reinforced composite shows better tensile strength of 12 MPa. Scanning electron microscope image analysis was carried out to examine the micro structure effect of composite in terms of tensile strength.

Czech name

—

Czech description

—

Type

D - Article in proceedings

CEP classification

JI - Composite materials

OECD FORD branch

—

Project

—

Continuities

S - Specificky vyzkum na vysokych skolach

Publication year

2016

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection

Engineering mechanics 2016

ISBN

978-80-87012-59-8

ISSN

1805-8248

e-ISSN

—

Number of pages

4

Pages from-to

482-485

Publisher name

Ústav termomechaniky AV ČR, v. v. i.

Place of publication

Praha

Event location

Svratka

Event date

Jan 1, 2016

Type of event by nationality

WRD - Celosvětová akce

UT code for WoS article

000379986700117