Thermo-mechanical Treatment of 0.4C-0.6Mn-2Si Steel with Various Soaking and Annealing Hold Temperatures
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F19%3A43954883" target="_blank" >RIV/49777513:23210/19:43954883 - isvavai.cz</a>
Result on the web
<a href="https://arl.ujep.cz/arl-ujep/cs/csg/?repo=ujeprepo&key=64208969632" target="_blank" >https://arl.ujep.cz/arl-ujep/cs/csg/?repo=ujeprepo&key=64208969632</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.21062/ujep/250.2019/a/1213-2489/mt/19/1/95" target="_blank" >10.21062/ujep/250.2019/a/1213-2489/mt/19/1/95</a>
Alternative languages
Result language
angličtina
Original language name
Thermo-mechanical Treatment of 0.4C-0.6Mn-2Si Steel with Various Soaking and Annealing Hold Temperatures
Original language description
Middle carbon low alloyed steel 0.4C-0.6Mn-2Si was subjected to thermo-mechanical treatment typical for TRIP (transformation induced plasticity steels). The processing consisted from soaking at the temperatures of 850-1000 °C and cooling at 30 °C/s to various annealing holds in bainite transformation temperature interval of 350-500 °C. During the cooling from the soaking temperature, two compressive deformations were carried out, the second one always at 720 °C. Resulting microstructures were analysed using light and scanning electron microscopy. X-ray diffraction phase analysis was carried out to establish volume fraction of retained austenite and mechanical properties were measured by tensile test. Tensile strengths in the region of 847-963 MPa were obtained and very good total elongations of 30-40% were achieved at the same time. Multiphase microstructures were obtained with various amounts of ferrite, bainite, retained austenite and pearlite.
Czech name
—
Czech description
—
Classification
Type
J<sub>SC</sub> - Article in a specialist periodical, which is included in the SCOPUS database
CEP classification
—
OECD FORD branch
20301 - Mechanical engineering
Result continuities
Project
<a href="/en/project/LO1502" target="_blank" >LO1502: Development of Regional Technological Institute</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2019
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Volume of the periodical
19
Issue of the periodical within the volume
01_2019
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
6
Pages from-to
95-100
UT code for WoS article
—
EID of the result in the Scopus database
2-s2.0-85063354603