Investigation of IMC Growth in Solder Joints
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23220%2F10%3A00503933" target="_blank" >RIV/49777513:23220/10:00503933 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
čeština
Original language name
Zkoumání růstu IMC v pájeném spoji
Original language description
This article deals with intermetallic layers which occure at the interface between solder and soldered material. To eliminate hazardous materials, only lead-free alloys, excluding special exemptions, are used today, not only in the Europe Union. Therefore, observing of creation of intermetallic compound between various lead-free soldering alloys and basic material is subject of wide interest. Many factors affect creating of intermetallic compounds, for example soldering temperature, constitution of solder, or setting of technological process of soldering. It depends, for example, on whether the solder joint is soldering by reflow oven, manually, by vapour phase soldering, or by dipping. Research of intermetallic compound growth in context of differentsoldering process setting, constitution of solder and artificial aging by raising thermal stress are presented in this article. The samples were divided into several groups to make comparison possible. One of these groups was leaved in ro
Czech name
Zkoumání růstu IMC v pájeném spoji
Czech description
This article deals with intermetallic layers which occure at the interface between solder and soldered material. To eliminate hazardous materials, only lead-free alloys, excluding special exemptions, are used today, not only in the Europe Union. Therefore, observing of creation of intermetallic compound between various lead-free soldering alloys and basic material is subject of wide interest. Many factors affect creating of intermetallic compounds, for example soldering temperature, constitution of solder, or setting of technological process of soldering. It depends, for example, on whether the solder joint is soldering by reflow oven, manually, by vapour phase soldering, or by dipping. Research of intermetallic compound growth in context of differentsoldering process setting, constitution of solder and artificial aging by raising thermal stress are presented in this article. The samples were divided into several groups to make comparison possible. One of these groups was leaved in ro
Classification
Type
O - Miscellaneous
CEP classification
JA - Electronics and optoelectronics
OECD FORD branch
—
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2010
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů