Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F14%3A43922869" target="_blank" >RIV/49777513:23520/14:43922869 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion
Original language description
The model of progressive failure of composite materials considering material non-linearity was developed and implemented into the Abaqus FE software. Extended Puck failure criterion for 3D stress state was used for failure prediction. Furthermore, a simplified approach for simulation of delamination was considered. For the progressive failure simulation, the stiffness matrix degradation was used and the degradation parameters were function of a fracture angle. The model was tested on problems of a pin-loaded composite plate and of a composite tube subjected to compressive loading perpendicular to the tube axis.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JI - Composite materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/ED1.1.00%2F02.0090" target="_blank" >ED1.1.00/02.0090: NTIS - New Technologies for Information Society</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach
Others
Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů