Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F16%3A43922879" target="_blank" >RIV/49777513:23520/16:43922879 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.17222/mit.2014.233" target="_blank" >http://dx.doi.org/10.17222/mit.2014.233</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.17222/mit.2014.233" target="_blank" >10.17222/mit.2014.233</a>

Result language
angličtina
Original language name
Model of Progressive Failure of Composite Materials using 3D Puck Failure Criterion
Original language description
The model of progressive failure of composite materials considering material non-linearity was developed and implemented into the Abaqus FE software. Extended Puck failure criterion for 3D stress state was used for failure prediction. Furthermore, a simplified approach for simulation of delamination was considered. For the progressive failure simulation, the stiffness matrix degradation was used and the degradation parameters were function of a fracture angle. The model was tested on problems of a pin-loaded composite plate and of a composite tube subjected to compressive loading perpendicular to the tube axis.
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)