High-performance thermochromic VO2-based coatings prepared on glass by a low-temperature scalable deposition

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F21%3A43963133" target="_blank" >RIV/49777513:23520/21:43963133 - isvavai.cz</a>

  • Alternative codes found

    RIV/49777513:23520/20:43960430

  • Result on the web

  • DOI - Digital Object Identifier

Alternative languages

  • Result language

    angličtina

  • Original language name

    High-performance thermochromic VO2-based coatings prepared on glass by a low-temperature scalable deposition

  • Original language description

    Three-layer thermochromic VO2-based coatings were prepared on soda-lime glass by a low-temperature scalable deposition technique. This deposition technique is based on reactive high-power impulse magnetron sputtering with a pulsed O2 flow control allowing us to prepare crystalline VO2 layers of the correct stoichiometry under highly industry-friendly deposition conditions: without any substrate bias at a low substrate temperature of 330 °C. Simultaneous doping of VO2 by W was performed to reduce the semiconductor-to-metal transition temperature to 20 °C. ZrO2 antireflection layers both below and above the thermochromic V0.982W0.018O2 layers were deposited at a low substrate temperature (&lt; 100 °C). A coating design utilizing a second-order interference in the ZrO2 layers was applied to increase both the luminous transmittance, Tlum, and the modulation of the solar transmittance, ΔTsol. The crystalline structure of the bottom ZrO2 layer further improved the VO2 crystallinity and the process reproducibility. The top ZrO2 layer provided the mechanical protection and environmental stability of the V0.982W0.018O2 layers. The ZrO2/ V0.982W0.018O2/ZrO2 coatings exhibited Tlum up to 60% at ΔTsol close to 6% for a V0.982W0.018O2 thickness of 45 nm, and Tlum up to 50% at ΔTsol above 10% for a V0.982W0.018O2 thickness of 69 nm.

  • Czech name

  • Czech description

Classification

  • Type

    O - Miscellaneous

  • CEP classification

  • OECD FORD branch

    20506 - Coating and films

Result continuities

  • Project

  • Continuities

    S - Specificky vyzkum na vysokych skolach

Others

  • Publication year

    2021

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů