Soldering steel sheets using soft solders
Original language description
The paper contains strength tests results of joints soldered using lead and leadless soft solders. For tests lead solders types Sn63Pb37, Sn60Pb40, Pb60Sn40 and Pb48Sn32Bi and leadless soft solders types Sn96Ag4, Sn99Cu1, Sn70Zn30 and Sn96Ag3Cu1 were used. As basic joint material steel sheet of 1.0 mm thickness and zinc-coated steel sheet of 1.0 mm thickness were used. The size of test specimen was 100 x 20 mm. Two sheets were always cleaned and jointed together. For heating the propane-butane plus airflame was used. The tested assemblies were loaded using the universal tensile-strength testing machine until their failure. At the tests the force needed for assemblies' failure and failure type (in the soldered joint, in the basic material) was recordedand the solder strength was calculated from the measured data. The test results show that for soldering of steel sheets as well of zinc-coated steel sheets of 1.0 mm thickness the joints soldered using the lead soft solder type Sn63Pb37
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JR - Other machinery industry
OECD FORD branch
—
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Research in Agricultural Engineering (Zemědělská technika)
ISSN
1212-9151
e-ISSN
—
Volume of the periodical
59
Issue of the periodical within the volume
4
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
6
Pages from-to
141-146
UT code for WoS article
—
EID of the result in the Scopus database
—