Effect of cyclic loading on modulus of elasticity of aspen wood

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41320%2F15%3A65016" target="_blank" >RIV/60460709:41320/15:65016 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.15376/biores.10.1.290-298" target="_blank" >http://dx.doi.org/10.15376/biores.10.1.290-298</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.15376/biores.10.1.290-298" target="_blank" >10.15376/biores.10.1.290-298</a>

Result language
angličtina
Original language name
Effect of cyclic loading on modulus of elasticity of aspen wood
Original language description
This article investigates the modulus of elasticity of solid and laminated aspen wood of various thicknesses after cyclic loading. A three-point static bending test was carried out to determine the modulus of elasticity. Cyclically loaded samples were compared with samples without cyclic loading. For the laminated wood, the results demonstrated a statistically significant impact of cyclic loading on the elasticity modulus. In contrast, no significant impact of cyclic loading was shown for the solid wood. The impact of the number of cycles was significant for both laminated and solid wood. When this number increased, the elasticity modulus values decreased. Generally, higher elasticity modulus values were confirmed for the laminated wood.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JI - Composite materials
OECD FORD branch
—

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)