Pseudocapacitive lithium storage in TiO2(B)

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388955%3A_____%2F05%3A00000604" target="_blank" >RIV/61388955:_____/05:00000604 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Pseudocapacitive lithium storage in TiO2(B)
Original language description
Phase-pure TiO2(B) with microfibrous morphology was prepared via a newly developed method from amorphous TiO2. Cyclic voltammetry evidences that Li-insertion into TiO2(B) is governed by a pseudocapacitive faradaic process, whose rate is not limited by solid-state diffusion of Li+ in a broad interval of scan rates. This unusual behavior was discussed in terms of the crystal structure of the TiO2(B) host, having freely accessible parallel channels for Li+-transport perpendicular to the (010) face. The characteristic Li-insertion electrochemistry of TiO2(B) allows re-interpretation of several previous reports, which did not consider explicitly this relation or the presence of TiO2(B) in various TiO2 materials of different origin.
Czech name
Pseudokapacitní akumulace lithia v TiO2(B)
Czech description
Byl vyvinut nový syntézní postup pro přípravu fázově čistého TiO2(B) s vláknitou morfologií. Cyklická voltametrie ukázala, že inserce lithia do uvedeného materiálu probíhá jako pseudokapacitní faradaický process, jehož rychlost není limitována difúzí Lidovnitř tuhé fáze pro široký interval rychlostí skenu.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
CG - Electrochemistry
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)