Remark on the Optical Gap in ZnO-Bi2O3-TeO2 Glasses

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F07%3A00085374" target="_blank" >RIV/61389013:_____/07:00085374 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Remark on the Optical Gap in ZnO-Bi2O3-TeO2 Glasses
Original language description
For ZnO-Bi2O3-TeO2 glasses the optical gap was determined at around 3.55 eV. The temperature dependence of the optical gap was also determined from the room temperature close up to 500K. Raman scattering measurements indicate that with a decrease in TeO2content, TeO4 trigonal bipyramid transformation proceeds into TeO3 trigonal pyramids.
Czech name
Poznámka k optické šířce zakázaného pásu ve sklech ZnO-Bi2O3-TeO2
Czech description
Pro skla ZnO-Bi2O3-TeO2 byly nalezeny hodnoty optické šířky zakázaného pásu kolem 3.55eV. Teplotní závislost optické šířky zakázaného pásu byla určena v teplotním intervalu od pokojové teploty až k teplotě blízko 500K. Měření Ramanova rozpylu indikuje transformaci TeO4 trigonálních bipyramid na TeO3 trigonální pyramidy s poklesem obsahu TeO2.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
CA - Inorganic chemistry
OECD FORD branch
—

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)