Properties and structure of Agx(As0.33S0.67)100-x bulk glasses

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F07%3A00086855" target="_blank" >RIV/61389013:_____/07:00086855 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Properties and structure of Agx(As0.33S0.67)100-x bulk glasses
Original language description
In this paper, bulk glasses with composition Agx(As33S67)100-x (x=0-25at%) were investigated. Amorphous structure of samples was confirmed by X-ray diffraction analysis. The structure was deduced from Raman spectra measured for all silver contents in theAs-S matrix.
Czech name
Vlastnosti a struktura skel Agx(As0.33S0.67)100-x
Czech description
Byly připraveny a zkoumány objemové vzorky o složení Ag(As33S67)100-x, (x=0-25at%). Amorfní struktura vzorků byla potvrzena rentgenovou strukturní analýzou. Struktura byla odvozena z Ramanovských spekter pro všechny obsahy stříbra v matrice As-S. Termální vlastnosti byly získány z modulované diferenciální skenovací kalorimetrie. Optické vlastnosti byly měřeny spektrální elipsometrickou spektroskopií. Indexy lomu byly vypočteny pomocí Cauchyho modelu. Všechna studovaná skla se chovají jako iontové vodiče. Příspěvek elektronové vodivosti k celkové vodivosti je velmi nízký a klesá k asi 0,01% pro sklo s 24at% Ag.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
CA - Inorganic chemistry
OECD FORD branch
—

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)