Post polymerisation hypercrosslinking of styrene/divinylbenzene poly(HIPE)s: creating micropores within macroporous polymer
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F14%3A00424542" target="_blank" >RIV/61389013:_____/14:00424542 - isvavai.cz</a>
Alternative codes found
RIV/67985858:_____/14:00424542
Result on the web
<a href="http://dx.doi.org/10.1016/j.polymer.2013.09.026" target="_blank" >http://dx.doi.org/10.1016/j.polymer.2013.09.026</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.polymer.2013.09.026" target="_blank" >10.1016/j.polymer.2013.09.026</a>
Alternative languages
Result language
angličtina
Original language name
Post polymerisation hypercrosslinking of styrene/divinylbenzene poly(HIPE)s: creating micropores within macroporous polymer
Original language description
Porous copolymers of styrene and divinylbenzene (DVB) were prepared by emulsion templating using high internal phase emulsions (HIPEs) as precursors for monoliths. The ratio of monomers was varied in order to obtain samples with different degrees of crosslinking and different amounts of unreacted vinyl groups originating from DVB. PolyHIPE monoliths were subjected to reswelling and treatment with a radical initiator. Significant enlargement of the amount of meso- and micropores in the material was foundresulting in a substantial increase of BET surface area, up to 7.2 times compared to untreated polyHIPEs. The treated PolyHIPE monoliths retained the open macroporous morphology typical of polyHIPE materials. Solid state 13C NMR experiments were used todetermine the amount of unreacted vinyl groups in polyHIPE samples, both before and after the hypercrosslinking treatment.
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JI - Composite materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/GA13-29009S" target="_blank" >GA13-29009S: Effects of filler surface on molecular mobility and resulting deformation and fracture behaviour of thermoplastic polymer composites</a><br>
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Polymer
ISSN
0032-3861
e-ISSN
—
Volume of the periodical
55
Issue of the periodical within the volume
1
Country of publishing house
GB - UNITED KINGDOM
Number of pages
6
Pages from-to
410-415
UT code for WoS article
000330207100052
EID of the result in the Scopus database
—