Influence of microstructure on sulphide stress cracking of hot rolled tubes

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F05%3A00012991" target="_blank" >RIV/61989100:27360/05:00012991 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Influence of microstructure on sulphide stress cracking of hot rolled tubes
Original language description
Paper summarizes results of sulphide stress cracking (SSC) resistance of tubes made of carbon steels. Quenching and tempering had a beneficial effect on SSC steel resistance despite the fact that mechanical properties and hardness increased considerably.Differences have been found in values of hydrogen diffusion coefficient for different structures.
Czech name
Vliv mikrostruktury na sulfidické praskání pod napětím za tepla válcovaných trubek
Czech description
Příspěvek shrnuje výsledky hodnocení odolnosti za tepla válcovaných trub z uhlíkových ocelí vůči sulfidickému praskání pod napětím. Kalení a popouštění mělo příznivý vliv na odolnost ocelí, i když došlo k nárůstu mechanických vlastností. Významné rozdílybyly nalezeny v hodnotách koeficientu difúze vodíku v ocelích pro rozdílné strukturní stavy.

Project
<a href="/en/project/GA106%2F04%2F0235" target="_blank" >GA106/04/0235: Sulphide stress cracking of modern structural steels</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)