Metallurgical aspects of rolling og magnesium alloy AZ91

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F05%3A00013062" target="_blank" >RIV/61989100:27360/05:00013062 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Metallurgical aspects of rolling og magnesium alloy AZ91
Original language description
Magnesium alloys have hexagonal structure and their forming is at normal temperatures very difficult, that`s why big plastic deformations are carried out in hot condition. The paper summarises results of experiments aimed at development of structure of modified alloy AZ91 at hot deformation. Deformation behaviour of alloy was verified at the temperature of 420°C by rolling. Initial structure was as část and after heat treatment T4
Czech name
Metalurgické aspekty tvářených Mg slitin AZ91
Czech description
Hořčíkové slitiny disponují hexagonální strukturou a jsou za normálních teplot obtížně tvařitelné, proto se velké plastické deformace realizují za tepla. V příspěvku jsou shrnuty výsledky experimentů zaměřených na vývoj struktury modifikované slitiny AZ91 při deformaci za tepla. Deformační chování slitiny bylo ověřeno na teplotě 420 °C válcováním. Výchozí struktura byla v litem stavu a ve stavu po tepelném zpracování T4

Project
<a href="/en/project/GA106%2F04%2F1346" target="_blank" >GA106/04/1346: Influence of unconventional deformation technology on formability, structure and mechanical properties of magnesium alloys</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)