Forging and rolling of magnesium alloy AZ61

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014166" target="_blank" >RIV/61989100:27360/06:00014166 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Forging and rolling of magnesium alloy AZ61
Original language description
The paper summarises results of experiments aimed at development of structure of modified alloy AZ61 at hot deformation. Deformation behaviour of alloy was verified at the temperature of 420ºC by rolling at 380ºC by forging respectivelly. Magnesium alloy AZ61 have hexagonál structure and thein forming is at room temperature very difficult, thatś why big plastic deformations are carried out in hot condition. After plastic deformations was obtained that original grain size decreased 15times.
Czech name
Kování a válcování hořčíkové slitiny AZ61
Czech description
Článek shrnuje výsledky experimentů získané vývojem struktury modifikované lsitiny AZ61 při deformaci za tepla. Deformační chování slitiny bylo ověřeno při teplotě 420ºC válcováním při 380ºC kováním resp. Slitina hořčíku AZ61 má hexagonální strukturu a jejich tváření při pokojové teplotě je velmi složité, to protože velké plastické deformace jsou uskutečněny při podmínkách za tepla. Po plastických deformacích byla získána původní velikost zrna snížena 15 krát.

Project
<a href="/en/project/GA106%2F04%2F1346" target="_blank" >GA106/04/1346: Influence of unconventional deformation technology on formability, structure and mechanical properties of magnesium alloys</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)