SUSCEPTIBILITY OF 304 SS-Ti BIMETAL TO HYDROGEN INDUCED CRACKING
Original language description
The work deals with evaluation of hydrogen induced cracking of 304 SS-Ti bimetal after explosive bonding. Both joined materials individually show a good resistance against hydrogen embrittlement. For bonded materials sinusoidal interface with curls is typical. In curls and in their vicinity intermetallic phases are often detected. Those represent hard and simultaneously more brittle areas which can be sensitive to hydrogen induced cracking. The bonding line can be also a potential position for hydrogenconcentration. After welding and exposition in corrosion solution bubbled with sulphide hydrogen the Ti of commercial purity and stainless steel 304 SS showed numerous thin cracks detected right in the intermetallic phases. The total crack sensitivity ratio (CSR), crack length ratio (CLR) and crack thickness ratio (CTR) were evaluated according the NACE Standard TM0284 item No. 21215. The results were confronted with the Specification 5L ANSI/API valid for OCTG. The work also includes ch
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regional materials science and technology centre</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Trends in the Development of Machinery and associated technology
ISSN
1840-4944
e-ISSN
—
Volume of the periodical
15
Issue of the periodical within the volume
1
Country of publishing house
BA - BOSNIA AND HERZEGOVINA
Number of pages
4
Pages from-to
173-176
UT code for WoS article
—
EID of the result in the Scopus database
—