HYDROGEN INDUCED CRACKING OF Ti CLAD TO THE 304 SS IN ANNEALED STATE
Original language description
Hydrogen induced cracking of Ti clad to the 304 SS in annealed state after explosive welding was investigated. The total crack sensitivity ratio (CSR), crack length one (CLR) and crack thickness ratio (CTR) according the NACE Standard TM0284 item No. 21215 were evaluated. The results were confronted with the 5L ANSI/API Specification valid for country tubular goods. Results were discussed on the basis of metallographic evaluation of the weld interface and its close neighbourhood. Numerous short and thick cracks were detected in materials of both processing types. After heat treatment, bimetal showed lower cracks count. Generally, the cracks were situated in the vicinity of bonding line of weld in intermetallic phases.
Czech name
—
Czech description
—

Project
<a href="/en/project/ED0040%2F01%2F01" target="_blank" >ED0040/01/01: Regional materials science and technology centre</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
METAL 2012 : 21st International Conference on Metallurgy and Materials : conference proceedings
ISBN
978-80-87294-31-4
ISSN
—
e-ISSN
—
Number of pages
6
Pages from-to
589-594
Publisher name
Tanger
Place of publication
Ostrava
Event location
Brno
Event date
May 23, 2012
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—

Similar results(10)