Microstructure, phase composition, and mechanical properties of Ti-Cr18/Ni10 clad metal
Original language description
Paper deals with chemical composition of interphase and weld of bimetal Ti clad Cr18/Ni10 and subsequently once and/or twice heat treated-HT (600 oC/1.5h/air) found by use of EDS and monochromatic hard X-ray (synchrotron). In both cases Fe2Ti was analysed in mixed zones only, where after one HT more than 17 % of mentioned intermetallic was detected being responsible for much higher defectiveness unlike welds after double HT where the portion of Fe2Ti was minimally 3 times lower. Thanks the double HT undesirable Fe2Ti particles were dissolved and thereby the stress in mixed zone was decreased.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
Explosive production of New Materials: Science, Technology, business, and Innovations : proceedings of the XIII. international symposium : June 20-24, 2016, Coimbra, Portugal
ISBN
978-989-99080-6-2
ISSN
—
e-ISSN
—
Number of pages
4
Pages from-to
121-124
Publisher name
University of Coimbra
Place of publication
Coimbra
Event location
Coimbra
Event date
Jun 20, 2016
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—

Similar results(10)