Filamentous Carbon Catalytic Deposition of coal-tar pitch fraction on corundum

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27640%2F07%3A00015369" target="_blank" >RIV/61989100:27640/07:00015369 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Filamentous Carbon Catalytic Deposition of coal-tar pitch fraction on corundum
Original language description
Our work was focused on deposition of volatile hydrocarbons of carbonaceous precursor on corundum wafer, taking advantage of a metallic catalyst incorporated in precursor. Coal tar-pitch, namely a fraction soluble in toluene, served as precursor materialfor deposition of filamentous material. The toluenesoluble fraction of tar-pitch originally contained metallic particles of iron and nickel. During heat treatment up to 10008C, metallic particles accompanied the volatile hydrocarbons conducive to forming a filamentous deposit. The deposit obtained demonstrates a semicrystalline material that has an irregular filamentous structure with an average filament diameter of 30 mm. The presence of catalysts after the deposition process was proved in the depositbut catalysts were not found in the residuum.
Czech name
Katalytická depozice vláknitých uhlíkatých materiálů na korundu
Czech description
Práce je zaměřená na depozici těkavých uhlovodíků - uhlíkatých prekurzorů na korundové podložce s využitím kovových katalyzátorů. Získaný depozit představuje semi-krystalický materiál, který má nepravidelnou vláknitou strukturu s průměrem vláken 30um.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JI - Composite materials
OECD FORD branch
—

Publication year
2007